As architects, builders and flooring contractors recognize the trouble free benefits of properly welded seams more areas of the building are being specified for heat welded floors. This creates a growing demand for qualified installers to install and heat weld commercial resilient flooring.
Following is a review of the basic tools and techniques used when heat welding homogeneous sheet vinyl flooring seams. Always follow manufacturer’s recommendations when working with their products.
In addition this author highly recommends the installer seek professional heat weld training from a trade organization, manufacturer, or a local distributor of commercial resilient flooring.
Prior to beginning a heat welded installation it is important for the installer to understand the construction of the material being installed. Product construction will affect:
Suitable substrates, acceptable concrete moisture test results.
Recommended adhesives, trowel notch, adhesive open and working times, recommended waiting period after floor installation to begin heat welding.
Groove depth, heat settings, welding tips or nozzles, and type of weld rod (thread).
Homogeneous constructed products are defined as having uniform structure or composition throughout, or in more technical terms it is the same on the bottom as it is on the top.
Homogeneous flooring can be constructed of PVC/ vinyl, rubber or alternative to PVC products. A sheet flooring product will be of a continuous length and of varying widths. Homogeneous flooring can be in a tile format, some of which can be heat welded.
The type of flooring will affect some of the techniques and materials used for heat welding. As previously mentioned this article will address heat welding homogeneous sheet vinyl flooring.
The material used for heat welding these types of flooring is PVC weld rod, also called a thread.
There are two main types of weld rod/ thread.
The most common weld rod is a round solid color (the diameter can vary from 2mm to 4 mm depending on the manufacturer). The colors of round weld rod can either blend with the flooring color or contrast with it to accent a design in the flooring. Color blended weld rods will hide small imperfections in groove width and straightness while grooves must be straight and of consistent width when contrasting color weld rod is used.
Another type of weld rod is the patterned or camouflage weld rod made of the same or similar color and pattern as the flooring. This type of rod blends well with the flooring and while it does not create an invisible seam, it does help to hide the seam.
A 1/64-inch gap in a seam
Depending on the manufacturer these weld rods can be a round or half round shape.
To create a successful heat welded seam, start with a well cut, well bonded seam.
Most manufacturers do not recommend butting factory edges together for a heat welded seam, 1/2 inch to 1 inch should be removed from each selvage for seaming. Typically a small gap (approximately 1/64”) should be left in the seam to help guide the grooving tool along the seam.
Depending on the adhesive and how much open time is required, there is generally a waiting period of 10- 24 hours to allow any residual liquid in the adhesive to dissipate prior to heat welding. Failure to allow residual liquid in the adhesive to dissipate can cause bond failure at the welded seam, which may not become apparent for several weeks to months after the installation.
The first step in heat welding is to groove the seam. For homogeneous sheet vinyl the groove should be 1/2 to 2/3 the thickness or gauge of the flooring and centered over the seam. A proper groove will provide the maximum surface on both sheets to create a strong weld. If the groove is too shallow or too deep, less surface is being welded together creating a weak weld. The groove width should be less than the diameter of the weld rod; for example a 3.5 mm groove will accommodate a 4mm weld rod.
There are three types of groovers used for heat welding.
The hand groover is useful for short seams and the ends of seams and walls for flash coving. These tools are impractical for long seams especially when contrasting color weld rod is used.
The rolling groover operates without electricity; these tools have the advantage of not creating dust and noise that can disrupt an existing jobsite. Some can also be used to accurately groove circles and curved seams, which is a great time saving feature.
Electric groovers are guided along the seam by the installer and cut a consistent groove in the seam, be careful to select a model with a dust bag and floating base to prevent digging the blade into the substrate.
Grooving and heat welding should be completed the same day to prevent contamination of grooves.
Grooving a circle with the Master TURBO Groover grooving tool
The next step is to weld the rod into the groove in the seam using a hot air gun equipped with a welding tip or nozzle.
The hot air gun provides the heat and airflow required to fuse the seam together. The heat elements on these guns can achieve temperatures as high as 600 degrees Celsius.
A blower transfers the heat to the groove in the seam and the weld rod. Hot air guns are available in hand held models and automatic welders. The hand held models are useful for short seams, small jobs and flash coving, and are still needed to complete seams when an automatic welder is used.
Automatic Welders are beneficial for long seams; they reduce ergonomic fatigue on the installer, and inconsistent welds (areas along the seam that get too hot or cold).
Special welding tips are attached to the hot air gun to focus the heat and air from the gun onto the groove and weld rod to simultaneously melt them together. The nozzle also allows the installer to apply a slight pressure to the weld helping to strengthen the weld.
Welding tips can vary from a pencil tip and feed roller to all types of speed tips or roller tips. The tips are designed to accommodate different weld rod diameters and shapes.
There are also tips designed for heat sensitive flooring, these tips reduce the airflow from the gun to heat only the rod and the groove. This prevents scorching or burning of wear surfaces on the material.
Prior to welding the installed flooring adjust the heat setting to the flooring manufacturers recommendations (if none are available adjust the heat to one half the heat capacity of the hot air gun and allow the gun to heat up for several minutes).
Using a scrap piece of the flooring practice grooving and welding to assure that the proper heat setting has been selected. This is an important step, even when heat welding the same products, as jobsite temperatures and extension cord length can affect how the hot air gun will perform. Another technique that is used to determine if the heat setting is correct is to place the weld rod in the hot air flow from the gun for a few seconds; the weld rod should melt without burning.
Be sure to select the correct welding tip/nozzle for the materials you are welding (the tip should accommodate the weld rod). Example; half round patterned weld rod will weld best using a triangular shaped tip. This prevents the weld rod from twisting and assures the correct surface of the rod melts into the groove.
Be aware that many newer commercial sheet floors are factory coated with UV cured urethane. These coatings can be sensitive to excessive heat. If scorching or cracking of the finish at the edges of the seam appears on your practice weld; adjust the heat setting, the angle of the welding tip to the floor, or use a heat sensitive type of welding tip.
A hot air gun with welding tip
To determine if the weld rod and flooring are melting together, make sure a slight ridge of material is forming on each side of the weld at the juncture of the weld rod and floor. This ridge is also known as a “wash”. No Wash -No Weld is a practical statement when heat welding.
A heat setting that is too high or moving the gun along the seam too slowly will burn the seam. This usually occurs as a widening of the wash and develops into a charred area along the seam.
A heat setting that is too low or moving along the seam too quickly will result in a cold spot in the weld and as the weld rod is being skived or trimmed it will pull out of the groove which will require repair.To determine if the weld rod and flooring are melting together, make sure a slight ridge of material is forming on each side of the weld at the juncture of the weld rod and floor. This ridge is also known as a “wash”. No Wash -No Weld is a practical statement when heat welding.
A heat setting that is too high or moving the gun along the seam too slowly will burn the seam. This usually occurs as a widening of the wash and develops into a charred area along the seam.
A heat setting hat is too low or moving along the seam too quickly will result in a cold spot in the weld and as the weld rod is being skived or trimmed it will pull out of the groove which will require repair.
In addition to establishing the correct temperature and speed it is very important to keep the welding tips clean to prevent clogging the tip. This can cause the weld rod to drag and stretch or break as it passes through the tip.
Most heat weld will be accomplished in two sections along the seam and will require a splice in the weld rod in the seam. Begin the seam at the wall, weld towards the opposite wall approximately three quarters of the seam.
Prepare the splice by trimming the completed end of the first weld either at an angle to the floor to create a ramp, or by using the skive knife and trim plate make the first pass along the seam. Remove any loose weld rod and cut or groove the end of the weld to create a ramp for the next weld. Avoid skiving the first welds flush to the floor as the splice in the weld will not hide as well.
Once this is completed begin welding from the opposite wall towards the first weld.
Weld up the ramp at the splice approximately one inch.
An automatic welder machine
This technique is also used to repair cold spots along a welded seam.
When welding seam intersections, such as cross seams, weld the short seam first using a skive knife or two layers of masking tape kept approximately one eighth inch from the edge of the groove, this will prevent burning the floor. Weld the seam onto the tape or metal which assures the end of the seam is welded. Once this is complete re-groove the end of the weld at the intersection of the long seam and then weld the seam.
The process of skiving or trimming the excess weld rod flush to the surface of the floor will be determined by which tools are being used.
If spatula or quarter moon knives are being used the seam will be skived in two passes.
The first pass is usually done while the weld rod is still warm, using a skive knife and trim plate or similar knife trim approximately one half the excess rod.
Then allow the remaining weld rod to cool completely to room temperature before making the final skiving pass.
These steps are very important to prevent a concave seam weld. If the weld rod is trimmed in one pass or while it is still warm, the rod will pull upward slightly as it is trimmed and will result in trimming too much of the rod. Concave seams become unsightly as dirt from foot traffic accumulates in the seam.
Tips for round and 1/2 round weld rod
A note on skiving knives, they are typically sharpened on one side to allow a flush cut along the floor surface. When using a trim plate it is a good practice to have two skive knives, one used exclusively with the trim plate and one to use for the flush cut. Using the same knife for both passes can leave scratch marks on the flooring as the trim plate can leave small nicks on the knife blade.
Wiping the seam with a clean rag dampened with a soap and water solution can help to prevent digging the knife into the surface of the flooring, however the most effective prevention is a sharp knife and a practiced hand.
The seam planer is a one pass tool that makes both cuts in one pass. When using a seam planer allow the weld to cool completely before skiving. Adjustable seam planers are beneficial for preventing digging in or skip when skiving.
As with skive knives maintain sharp, clean blades on seam planers.
One pass Turbo plane
When skiving and any repairs are completed, depending on the product and manufacturer, there may be additional requirements for heat glazing the weld rod.
The heat glazing process is accomplished with a hand held hot air gun with a pencil tip set to a lower temperature. Hot air is focused along the finished weld giving the weld a glossy appearance. This slightly consolidates the weld rod which helps to keep it clean. Additionally some manufacturers may require a treatment of chemical seam sealer on the finished weld. Finally it is a good practice to apply a coat of commercial floor sealer or polish over the seam to keep it clean until construction is completed and regular floor maintenance begins.
In summary, with the proper tools and practice, installers will enhance the services they offer and create another source of income that is not as physically demanding as other aspects of the trade can be.
While advances in heat welding tools make the job easier and more efficient, as with anything, practice makes perfect; or, pros practice.